Sumitube® SA3 |
|
|
|
Dual Wall Polyolefin, 4:1
Operating Temperature: -40 up to 125°C |
|
|
|
ASTM
SAE J 1128
SUMITOMO Standard |
|
Surface:
Matt
Marking: None |
 |
|
|
Dimensions |
|
BEFORE SHRINKAGE |
AFTER SHRINKAGE |
DELIVERY UNITS
* |
|
Inner diameter
(EID) min. |
Inner diameter
(RID) max. |
Wall thickness
(RWT) min-max |
Unit quantity |
Box quantity |
|
[type] |
[mm] |
[mm] |
[mm] |
[m] |
[m] |
|
5,8/1,2 |
5,80 |
1,26 |
nom. 1,40 |
60 |
300 |
|
7,5/1,6 |
7,50 |
1,64 |
nom. 1,75 |
60 |
300 |
|
10,9/2,4 |
10,9 |
2,40 |
nom. 2,20 |
30 |
150 |
|
17,8/4,4 |
17,8 |
4,45 |
nom. 2,80 |
18 |
90 |
|
* Standard packaging: Cut lenght of 1200mm. |
|
|
Colours & Technical drawing |
|
|
|
|
SPECIAL COLOURS |
|
upon request |
|
|
|
|
TECHNICAL DRAWING |
|
 |
|
|
| |
©
2009 SUMITOMO
ELECTRIC Schrumpf-Produkte GmbH. Subject to change. Tube colours may vary. |
SUMITOMO-G-06022012 PM0707 |
|
|
|
|
Sumitube® SA3 |
|
|
|
Dual Wall Polyolefin, 4:1 |
|
|
|
|
|
Technical properties |
|
PHYSICAL PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Longitudinal Change |
ASTM |
-5% ± 5% |
-5% |
|
Tensile Strength |
ASTM D 2671 |
Min. 10,4 MPa |
≥ 14 MPa |
|
Elongation at Break |
ASTM D 2671 |
Min. 300% |
≥ 450% |
|
Secant Modulus |
ASTM D 2671 |
Min. 150 MPa |
≥ 160 MPa |
|
THERMAL PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Operating Temperature |
Life-Curve |
-40 up to 125°C |
-40 up to 125°C |
|
Min. Shrink Temperature |
Arrhenius-Plot |
full recovery |
130°C |
|
Shrinking starts at |
Arrhenius-Plot |
|
100°C |
|
Heat Shock (225°C x 4h) |
ASTM D 2671 |
no cracking |
Pass |
|
CHEMICAL PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Flammability (outer jacket only) |
SAE J 1128 |
Extinguishing within 70 seconds |
Pass |
|
Water Absorption |
ASTM D 570 |
Max. 1,0% |
0,5% |
|
Leakage current after fluids immersion |
ES-A-603-D |
Max. 0,25 µAMPs |
≤ 0,20 µAMPs |
|
ELECTRICAL PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Volume Resistivity |
ASTM D 876 |
Min. 1012 Ω·cm |
≥ 1013 Ω·cm |
|
Dielectric Strength |
ASTM D 876 |
Min. 15 kV/mm |
≥ 20 kV/mm |
|
OTHER PROPERTIES |
|
PROPERTY |
TEST METHOD |
REQUIREMENT |
TYPICAL VALUE |
|
Dynamic cut through |
ASTM D 3032 |
Min. 134 N |
≥ 140 N |
|
Leakage current test |
ES-A-603-D |
Max. 0,25 µAMPs |
≤ 0,20 µAMPs |
|
Thermal humidity cycling (15 cycles) |
15 cycles (16hrs/40°C/95-98% R.H) |
no cracks or pinholes and Max. 0,25 µAMPs leakage current |
Pass |
|
Thermal ageing (125°C x 1008h) |
125°C x 1008h |
no cracks or pinholes and Max. 0,25 µAMPs leakage current |
Pass |
|
Thermal shock-cycles |
125 shock- cycles (-40°C x 30min / +125°C x 30 min) |
no cracks or pinholes and Max. 0,25 µAMPs leakage current |
Pass |
Tested fluids:
ASTM-Oil #3. Power steering fluid. Automatic transmission fluid.
Engine coolant. (2 hrs at 100°C).
Diesel fuel . Windshield cleaner. ASTM Fuel C.
Engine cleaner. (2 hrs at 23°C).
SAE J 1703 bracke fluid. (2 hrs at 50°)C. |
|
| |
©
2009 SUMITOMO
ELECTRIC Schrumpf-Produkte GmbH. Subject to change. Tube colours may vary. |